隨著輕質(zhi)隔墻(qiang)(qiang)板(ban)材料的(de)大量應用(yong)，輕質(zhi)隔墻(qiang)(qiang)板(ban)的(de)一些問(wen)題也不斷出現，主要問(wen)題是墻(qiang)(qiang)體裂(lie)縫的(de)產生。本文將對(dui)輕質(zhi)隔墻(qiang)(qiang)板(ban)的(de)裂(lie)縫進行分析，并對(dui)輕質(zhi)隔墻(qiang)(qiang)板(ban)的(de)裂(lie)縫進行預(yu)防。

一、 輕質隔(ge)墻板(ban)裂(lie)縫分析

為了找出輕質隔(ge)(ge)墻(qiang)板(ban)(ban)裂(lie)縫產(chan)生的(de)原因，我們發現輕質隔(ge)(ge)墻(qiang)板(ban)(ban)裂(lie)縫主(zhu)要(yao)分布在板(ban)(ban)與(yu)板(ban)(ban)之(zhi)間的(de)接縫處；板(ban)(ban)與(yu)梁之(zhi)間的(de)接縫；門窗洞口周圍；局部有裂(lie)紋；抹灰面空(kong)鼓造成(cheng)的(de)不規(gui)則(ze)裂(lie)縫。經過技(ji)術分析，產(chan)生開裂(lie)的(de)主(zhu)要(yao)原因有以下(xia)幾點

1.輕質隔墻板收(shou)縮率過(guo)高

墻(qiang)(qiang)板(ban)(ban)安裝(zhuang)現場觀察(cha)發(fa)現，墻(qiang)(qiang)板(ban)(ban)上無(wu)包裝(zhuang)物，墻(qiang)(qiang)板(ban)(ban)表面(mian)有濕(shi)痕。經(jing)抽(chou)檢，運(yun)抵現場的墻(qiang)(qiang)板(ban)(ban)干縮(suo)(suo)率(lv)(lv)達到1mm/m左右。墻(qiang)(qiang)板(ban)(ban)干縮(suo)(suo)率(lv)(lv)過大，超過標準要(yao)求。經(jing)分析，干縮(suo)(suo)率(lv)(lv)是(shi)導致(zhi)墻(qiang)(qiang)板(ban)(ban)開(kai)裂的主(zhu)要(yao)因素，而(er)高干縮(suo)(suo)率(lv)(lv)是(shi)導致(zhi)墻(qiang)(qiang)板(ban)(ban)開(kai)裂的主(zhu)要(yao)原因之一。

2、施(shi)工(gong)工(gong)藝(yi)不合理造成墻板裂(lie)縫

通過實際(ji)調查，發現墻板(ban)開裂的方式有：沿(yan)(yan)柱邊和梁邊開裂；砂(sha)漿(jiang)斷裂產生裂縫(feng)(feng)；裂紋沿(yan)(yan)著板(ban)的邊緣產生。經分(fen)析(xi)，在施工過程中，墻體及板(ban)邊基(ji)層(ceng)有較多灰塵(chen)、油(you)污；砂(sha)漿(jiang)強(qiang)度不夠；砂(sha)漿(jiang)有裂縫(feng)(feng)。經分(fen)析(xi)，不合理(li)的施工工藝導致砂(sha)漿(jiang)粘(zhan)結(jie)強(qiang)度低(di)，也(ye)是(shi)造成墻板(ban)裂縫(feng)(feng)的主要原因(yin)之一。

3、養護(hu)不(bu)合理(li)造成墻(qiang)板開裂(lie)

經現場觀察發現，墻板安裝2-3天后，部(bu)分施(shi)工企業(ye)(ye)開(kai)始(shi)進行墻體(ti)二(er)次作業(ye)(ye)。通過分析(xi)，砂(sha)漿(jiang)強度在2-3天內(nei)明顯不(bu)足，此(ci)時對墻體(ti)進行第(di)二(er)次操作容易造成砂(sha)漿(jiang)裂縫。因此(ci)，輕質隔墻板施(shi)工維護不(bu)合理也是(shi)造成墻板開(kai)裂的原(yuan)因之一(yi)。

二、 輕質(zhi)隔墻板的(de)防裂措(cuo)施

根據輕(qing)質隔(ge)墻(qiang)板(ban)(ban)裂(lie)(lie)縫(feng)產生的(de)(de)原(yuan)因，在輕(qing)質隔(ge)墻(qiang)板(ban)(ban)安裝過(guo)(guo)程中，嚴格控制墻(qiang)板(ban)(ban)的(de)(de)干縮率，優化和改進(jin)施工(gong)工(gong)藝，并對墻(qiang)板(ban)(ban)進(jin)行(xing)合(he)理的(de)(de)工(gong)后養護。經過(guo)(guo)3天和5天的(de)(de)現(xian)場(chang)觀察(cha)，發現(xian)安裝施工(gong)后的(de)(de)墻(qiang)板(ban)(ban)沒有裂(lie)(lie)縫(feng)。實(shi)踐證明，通過(guo)(guo)嚴格控制產品質量(liang)，改進(jin)不合(he)理的(de)(de)施工(gong)工(gong)藝，做好墻(qiang)板(ban)(ban)的(de)(de)后期(qi)維護，可以達到輕(qing)質隔(ge)墻(qiang)板(ban)(ban)防裂(lie)(lie)的(de)(de)目的(de)(de)。輕(qing)質隔(ge)墻(qiang)板(ban)(ban)裂(lie)(lie)縫(feng)的(de)(de)預防措施總結如下：

1.減少輕質隔墻板的干燥收縮。

首先，在(zai)墻(qiang)板(ban)(ban)(ban)(ban)生產過(guo)程中(zhong)，要求廠家按規范要求保證(zheng)墻(qiang)板(ban)(ban)(ban)(ban)的(de)(de)養(yang)護期(qi)必須達到28天(tian)，強(qiang)度必須達到一致(zhi)；第(di)二，經過(guo)28天(tian)的(de)(de)養(yang)護后，將墻(qiang)板(ban)(ban)(ban)(ban)干燥，含水(shui)率控制在(zai)5%以內(nei)。經實(shi)際數據檢驗，干燥后墻(qiang)板(ban)(ban)(ban)(ban)的(de)(de)干縮(suo)(suo)小于0.4mm/m，干燥前墻(qiang)板(ban)(ban)(ban)(ban)的(de)(de)干縮(suo)(suo)約為0.8mm/m；后面(mian)要求廠家提供的(de)(de)墻(qiang)板(ban)(ban)(ban)(ban)要做好(hao)塑料密封(feng)，運輸過(guo)程中(zhong)要嚴格(ge)注意防水(shui)處理，確(que)保墻(qiang)板(ban)(ban)(ban)(ban)安(an)裝前的(de)(de)狀態與干燥后的(de)(de)狀態一致(zhi)。通(tong)過(guo)技術分(fen)析，通(tong)過(guo)以上手段控制墻(qiang)板(ban)(ban)(ban)(ban)的(de)(de)干縮(suo)(suo)，裂縫發生概率可降低(di)50%。

2.改進墻板施工工藝。

根據墻板(ban)(ban)(ban)(ban)裂(lie)縫(feng)(feng)(feng)主要發生(sheng)在(zai)(zai)板(ban)(ban)(ban)(ban)與(yu)板(ban)(ban)(ban)(ban)之(zhi)(zhi)間(jian)(jian)的(de)(de)(de)接(jie)(jie)縫(feng)(feng)(feng)、與(yu)柱、梁的(de)(de)(de)接(jie)(jie)縫(feng)(feng)(feng)以及門窗(chuang)洞口(kou)(kou)周(zhou)圍的(de)(de)(de)特點，通(tong)過技術(shu)分(fen)析(xi)(xi)，認為主要原因(yin)是接(jie)(jie)縫(feng)(feng)(feng)處(chu)(chu)砂(sha)漿(jiang)(jiang)不(bu)夠飽滿，而且砂(sha)漿(jiang)(jiang)與(yu)墻板(ban)(ban)(ban)(ban)之(zhi)(zhi)間(jian)(jian)的(de)(de)(de)縫(feng)(feng)(feng)隙粘(zhan)(zhan)結不(bu)好，造(zao)成板(ban)(ban)(ban)(ban)與(yu)板(ban)(ban)(ban)(ban)之(zhi)(zhi)間(jian)(jian)、板(ban)(ban)(ban)(ban)與(yu)柱、梁之(zhi)(zhi)間(jian)(jian)的(de)(de)(de)抗拉強度不(bu)足，在(zai)(zai)施工時出(chu)(chu)現裂(lie)縫(feng)(feng)(feng)經過總結分(fen)析(xi)(xi)，對墻板(ban)(ban)(ban)(ban)安裝工藝進(jin)(jin)行了改進(jin)(jin)。首(shou)先對接(jie)(jie)縫(feng)(feng)(feng)處(chu)(chu)構(gou)件的(de)(de)(de)基層進(jin)(jin)行清(qing)理，清(qing)除(chu)表面的(de)(de)(de)灰(hui)塵(chen)和(he)油污，然后涂上界面劑，提(ti)高砂(sha)漿(jiang)(jiang)與(yu)構(gou)件的(de)(de)(de)粘(zhan)(zhan)結強度；其次，采用(yong)“后澆法”澆筑接(jie)(jie)縫(feng)(feng)(feng)處(chu)(chu)的(de)(de)(de)砂(sha)漿(jiang)(jiang)。擴(kuo)大接(jie)(jie)縫(feng)(feng)(feng)間(jian)(jian)距，在(zai)(zai)板(ban)(ban)(ban)(ban)間(jian)(jian)、板(ban)(ban)(ban)(ban)柱間(jian)(jian)、梁間(jian)(jian)形(xing)成后澆帶，保證(zheng)砂(sha)漿(jiang)(jiang)能(neng)完全灌入接(jie)(jie)縫(feng)(feng)(feng)；門窗(chuang)洞口(kou)(kou)四個陽(yang)角處(chu)(chu)鋪設玻璃纖維網格布，提(ti)高接(jie)(jie)縫(feng)(feng)(feng)處(chu)(chu)砂(sha)漿(jiang)(jiang)粘(zhan)(zhan)結強度。經過技術(shu)分(fen)析(xi)(xi)和(he)現場觀(guan)察，通(tong)過以上施工工藝改進(jin)(jin)，墻板(ban)(ban)(ban)(ban)出(chu)(chu)現裂(lie)縫(feng)(feng)(feng)的(de)(de)(de)概率降低了30%。

3、施工后對墻板進行合理養護。

墻(qiang)板安裝后，接(jie)縫(feng)處(chu)砂漿應合理養護(hu)，養護(hu)時間不少于7天。

在(zai)此基礎上(shang)，通過控(kong)制墻(qiang)(qiang)板(ban)的(de)干(gan)縮率，改(gai)進墻(qiang)(qiang)板(ban)的(de)施(shi)工(gong)工(gong)藝(yi)(yi)，合理養護，可以防止輕(qing)質(zhi)隔墻(qiang)(qiang)板(ban)的(de)裂(lie)縫。經現場觀察分析，采用(yong)上(shang)述防治措施(shi)2年(nian)和4年(nian)，墻(qiang)(qiang)板(ban)均未出(chu)現裂(lie)縫。隨著我國城市(shi)化進程(cheng)的(de)不(bu)斷發展，考慮(lv)到(dao)(dao)輕(qing)質(zhi)隔墻(qiang)(qiang)板(ban)在(zai)節能、環保、廢物利用(yong)、防火(huo)等方面的(de)綜合優勢(shi)，輕(qing)質(zhi)隔墻(qiang)(qiang)板(ban)的(de)應用(yong)將更加廣泛。同時，考慮(lv)到(dao)(dao)傳統輕(qing)質(zhi)隔墻(qiang)(qiang)板(ban)存在(zai)的(de)一些質(zhi)量通病，有(you)必要加強(qiang)新型節能墻(qiang)(qiang)體材料的(de)研究和施(shi)工(gong)工(gong)藝(yi)(yi)的(de)優化，以滿足市(shi)場的(de)進一步需(xu)求。